对2219铝合金搅拌摩擦焊接头中出现的未焊透和孔洞缺陷进行一次、二次搅拌摩擦补焊实验。结果表明：在合适的补焊工艺参数下,可有效消除接头原有缺陷,获得成形美观,性能良好的接头;随补焊次数的增加,接头软化区域显著增加;含有上述两种缺陷接头一次补焊后拉伸性能显著提高,二次补焊接头相比于一次补焊接头拉伸性能有所降低;含有缺陷的原始接头拉伸时均于缺陷处起裂导致接头塑性较低,补焊后接头都断裂于后退侧热影响区与热机影响区交界处,呈韧性断裂模式。     

Comparative survival analysis of Deinococcus radiodurans and the haloarchaea Natrialba magadii and Haloferax volcanii exposed to vacuum ultraviolet irradiation

The haloarchaea Natrialba magadii and Haloferax volcanii, as well as the radiation-resistant bacterium Deinococcus radiodurans, were exposed to vacuum UV (VUV) radiation at the Brazilian Synchrotron Light Laboratory. Cell monolayers (containing 10(5) to 10(6) cells per sample) were prepared over polycarbonate filters and irradiated under high vacuum (10(-5) Pa) with polychromatic synchrotron radiation. N. magadii was remarkably resistant to high vacuum with a survival fraction of (3.77±0.76)×10(-2), which was larger than that of D. radiodurans (1.13±0.23)×10(-2). The survival fraction of the haloarchaea H. volcanii, of (3.60±1.80)×10(-4), was much smaller. Radiation resistance profiles were similar between the haloarchaea and D. radiodurans for fluences up to 150?J m(-2). For fluences larger than 150?J m(-2), there was a significant decrease in the survival of haloarchaea, and in particular H. volcanii did not survive. Survival for D. radiodurans was 1% after exposure to the higher VUV fluence (1350?J m(-2)), while N. magadii had a survival lower than 0.1%. Such survival fractions are discussed regarding the possibility of interplanetary transfer of viable microorganisms and the possible existence of microbial life in extraterrestrial salty environments such as the planet Mars and Jupiter's moon Europa. This is the first work to report survival of haloarchaea under simulated interplanetary conditions.     

Microbial fuel cells applied to the metabolically based detection of extraterrestrial life

Since the 1970s, when the Viking spacecrafts carried out experiments to detect microbial metabolism on the surface of Mars, the search for nonspecific methods to detect life in situ has been one of the goals of astrobiology. It is usually required that a methodology detect life independently from its composition or form and that the chosen biological signature point to a feature common to all living systems, such as the presence of metabolism. In this paper, we evaluate the use of microbial fuel cells (MFCs) for the detection of microbial life in situ. MFCs are electrochemical devices originally developed as power electrical sources and can be described as fuel cells in which the anode is submerged in a medium that contains microorganisms. These microorganisms, as part of their metabolic process, oxidize organic material, releasing electrons that contribute to the electric current, which is therefore proportional to metabolic and other redox processes. We show that power and current density values measured in MFCs that use microorganism cultures or soil samples in the anode are much larger than those obtained with a medium free of microorganisms or sterilized soil samples, respectively. In particular, we found that this is true for extremophiles, which have been proposed as potential inhabitants of extraterrestrial environments. Therefore, our results show that MFCs have the potential to be used for in situ detection of microbial life.     

电子束焊接Ti-45Al-1.7Cr-1.7Nb双相钛铝合金组织结构及其裂纹形成机制

研究了电子束焊接Ti-45Al-1.7Cr-1.7Nb双相钛铝合金的接头组织形态及裂纹形成机制.形成裂纹的主要原因是热致应力的产生;冷速过快导致α相分解受到抑制,α2与γ相间的热膨胀系数的差异,以及形成的层片状结构板束间距变化也对裂纹的产生有着重要影响.采用散焦预热、增大焊接线能量可有效防止焊接TiAl固相裂纹的产生.     

镍基高温合金电子束钎焊润湿性及界面产物

采用两种钎料对镍基高温合金进行了真空电子束钎焊润湿性试验,探讨了真空电子束钎焊主要工艺参数对钎料铺展润湿性的影响.在确定优选钎料的基础上,进行了电子束钎焊搭接试验,研究了界面结构,确定了界面反应产物及其形态分布.     

锡青铜与钢的扩散连接

研究了ＱＳｎ４－４－２．５锡青铜与４５＾＃钢的扩散连接,以及工艺参数对接头性能的影响,确定了锡青铜与钢扩散连接的最佳工艺参数：连接温度Ｔ＝８２０℃－８５０℃,连接压力Ｐ＝１．０ＭＰａ－２．０ＭＰａ,连接时间ｔ＝２０ｍｉｎ,接头抗拉强度可达１８０Ｍａ以上,并运用金相,扫描电镜对接头进行了微观分析。     

SiC_p/Al复合材料焊接技术的研究现状与展望北大核心CSCD

阐述了SiCp/Al复合材料(PEA)焊接过程中的常见问题及相应的解决措施。对国内外PEA焊接的研究进展进行了综述及评价,并且对其发展前景进行了展望。     

Ti-6Al-4V电子束焊接焊缝区域精细组织特征

采用OM,XRD,EPMA,TEM分析了电子束焊接Ti-6Al-4V焊缝区域的精细组织结构特征。结果表明接头区域组织形态由基体等轴晶向焊缝柱状形态演化,焊缝区域呈现单一α′网篮状组织,TEM板束形态呈多向分布,焊缝区域的位错分布密度与基体母材相比呈现出减小的趋势,且熔合线附近存在V,Fe等β稳定元素浓度起伏现象。     

Remarks on “A new non-specificity measure in evidence theory based on belief intervals”

Two types of uncertainty co-exist in the theory of evidence: discord and non-specificity. From 90s, many mathematical expressions have arisen to quantify these two parts in an evidence. An important aspect of each measure presented is the verification of a coherent set of properties. About non-specificity, so far only one measure verifies an important set of those properties. Very recently, a new measure of non-specificity based on belief intervals has been presented as an alternative measure that quantifies a similar set of properties (Yang et al., 2016). It is shown that the new measure really does not verify two of those important properties. Some errors have been found in their corresponding proofs in the original publication.     

搅拌摩擦焊匙孔修复技术研究现状

搅拌摩擦焊虽是一种环保高效的固态连接方法,但在收焊处遗留的匙孔却难以避免,往往需要对匙孔进行修复.本文综述了搅拌摩擦焊匙孔修复技术国内外研究现状,指出了匙孔修复对采用搅拌摩擦焊结构的重要性,为实际生产过程中搅拌摩擦焊缝匙孔修复提供参考.